Introduction
410 stainless steel is a martensitic stainless steel produced in accordance with the American ASTM standard. It has a carbon content of approximately 0.15% and a chromium content ranging from 11.5% to 13.5%. This material exhibits high strength and hardness, good hardenability, and will harden after heat treatment. It is also magnetic.
| 回火温度(Tempering Temp.) | 抗拉强度(≥MPa) | 屈服强度(≥MPa) | 伸长率(≥%) | 布氏硬度(HB) |
|---|---|---|---|---|
| 200°C(392°F) | 1380 | 1100 | 10 | 388 - 444 |
| 315°C(600°F) | 1170 | 965 | 12 | 341 - 388 |
| 425°C(800°F) | 1030 | 860 | 14 | 302 - 341 |
| 540°C(1000°F) | 860 | 725 | 16 | 255 - 302 |
| 650°C(1200°F) | 725 | 620 | 18 | 223 - 255 |
Corresponding Grades Under International Standards
American ASTM Standard: 410, UNS S41000
Japanese JIS Standard: SUS410
Chinese GB Standard: 12Cr13
German DIN Standard: X12Cr13 (Designation: 1.4006)
Performance Characteristics
It has good machinability, high strength, and can be strengthened through heat treatment. Meanwhile, it possesses a certain level of corrosion resistance, showing anti-corrosion performance in mild atmospheres, steam, and many mild chemical environments. However, it is not suitable for harsh corrosive environments.
Specification and Dimensions
The thickness of 410 stainless steel sheets generally ranges from 0.08mm to 8.0mm. Common widths include 1000mm, 1219mm, and 1500mm. The length can be customized according to requirements, with typical options such as 2000mm, 2440mm, and 3000mm.
Application Fields
It is commonly used to manufacture components that require both strength, hardness, and a certain degree of corrosion resistance. Typical applications include tableware, steam and gas turbine blades, bolts, nuts, pump and valve parts, as well as dental and surgical instruments.
Top Three Questions and Answers:
Hot Tags: sus410 s41000 sts410 1.4006 12cr13 410 stainless steel sheet, China sus410 s41000 sts410 1.4006 12cr13 410 stainless steel sheet manufacturers, suppliers, factory, ferrite stainless steel showers, ferrite stainless steel industrial grade, ferrite stainless steel bending, ferrite stainless steel appliances, ferrite stainless steel elevators, ferrite stainless steel refrigerators